Jan 4 2002
|
Grade
|
UNS No.
|
Density
|
Elastic Modulus
|
Mean Coeff of Thermal Expansion μm/m/°C (b)
|
Thermal Conductivity
|
Specific Heat
|
Electrical Resistivity
|
|
|
|
kg/m3
|
GPa(a)
|
0-100°C
|
0-315°C
|
0-538°C
|
At 100°C W/m.K
|
At 500°C W/m.K
|
0-100°C J/kg.K
|
nΩ.m
|
|
201
202
301
302
302B
303
304
304L
302HQ
304N
305
308
309
310
314
316
316L
316N
317
317L
321
329
330
347
384
409
410
416
420
430
430F
431
434
436
440C
444
446
630
631
904L
2111HTR
2205
2304
2507
3CR12
4565S
UR52N+
Zeron100
|
S20100
S20200
S30100
S30200
S30215
S30300
S30400
S30403
S30430
S30451
S30500
S30800
S30900
S31000
S31400
S31600
S31603
S31651
S31700
S31703
S32100
S32900
N08330
S34700
S38400
S40900
S41000
S41600
S42000
S43000
S43020
S43100
S43400
S43600
S44004
S44400
S44600
S17400
S17700
N08904
S30815
S31803
S32304
S32750
S41003
S34565
S32520
S32760
|
7860
7860
8000
7900
8000
8000
7900
7900
8000
8000
8000
8000
8000
8000
7800
8000
8000
7920
8000
8000
7920
7800
8000
8000
8000
7800
7750
7800
7800
7800
7800
7750
7800
7800
7650
7800
7800
7750
7800
8000
7800
7805
7800
7800
7740
8000
7820
7840
|
207
211
193
200
195
193
200
200
193
196
193
195
200
200
200
193
193
196
195
200
193
186
197
195
193
200
200
200
200
200
200
200
200
200
200
200
200
196
204
200
200
200
200
200
200
190
200
190
|
16.6
17.5
16.6
16.6
16.2
17.2
16.6
16.6
17.3
17.2
17.3
17.3
14.9
15.8
-
16
15.9
16
16
16.5
16.6
10.1
14.4
17.3
17.3
11.7
9.9
9.9
10.3
10.4
10.4
10.2
10.4
10.4
10.1
10.0
10.4
10.8
11.0
15.0
17.0
13.7
13.0
13.0
10.8
14.5
13.5
12.6
|
17.5
18.4
17.2
17.8
18.0
17.8
17.8
17.8
17.8
17.8
17.8
17.8
16.7
16.2
15.1
16.2
16.2
16.2
16.2
-
17.2
11.5
16.0
17.8
17.8
11.7
11.4
11.0
10.8
11.0
11.2
12.1
11.0
11.0
10.3
10.6
10.8
11.6
11.6
-
17.2
14.7
-
14.0
11.3
16.3
14.0
13.9
|
18.4
19.2
18.2
18.4
19.4
18.4
18.4
18.4
18.4
18.4
18.4
18.4
17.3
16.9
-
17.5
17.5
17.5
17.5
18.1
18.6
-
16.7
18.6
18.4
12.4
11.6
11.5
11.7
11.4
11.9
-
11.4
11.3
11.7
11.4
11.2
-
-
-
18.0
-
-
-
12.5
17.2
14.5
-
|
16.3
16.2
16.3
16.3
15.9
16.2
16.3
16.3
16.3
16.3
16.3
15.2
15.6
14.2
17.5
16.3
16.3
14.4
16.2
14.4
16.1
-
-
16.1
16.3
25.8
24.9
24.9
24.9
26.1
26.1
20.2
26.1
23.9
24.2
26.8
20.9
18.4
16.4
13.0
14.0
19.0
16.0
17.0
30.5
14.5
17.0
14.4
|
23
21.6
21.4
21.4
21.6
21.5
21.4
21.5
21.5
21.5
21.5
21.6
18.7
18.7
20.9
21.5
21.5
-
21.5
-
22.2
-
-
22.2
21.5
27.5
28.7
28.7
-
26.3
26.3
-
26.3
26.0
-
-
24.4
22.7
21.8
-
18.0
-
-
-
40.0
-
-
-
|
502
500
500
500
500
500
500
500
502
500
500
500
500
500
500
500
500
500
500
500
500
460
460
500
500
460
460
460
460
460
460
460
460
460
460
420
500
460
460
500
500
450
470
470
480
510
450
480
|
670
690
720
720
720
720
720
720
720
720
720
720
780
780
770
740
740
740
740
740
720
750
1020
730
790
600
570
570
570
600
600
720
600
600
600
620
640
800
830
850
850
850
850
-
570
920
850
850
|
(a) 1 GPa = 1000 MPa
(b) μm/m/°C = x10-6/°C
Magnetic permeability of all 300 annealed austenitic steels is approximately 1.02.