Introduction
Alloy steels are designated by AISI four-digit numbers and are more susceptible to heat and mechanical treatments than carbon steels. They comprise different kinds of steels having compositions which exceed the limitations of Va, Cr, Si, Ni, Mo, C and B in the carbon steels.
The following datasheet will give an overview of AISI A514 grade H alloy steel.
Chemical Composition
The chemical composition of AISI A514 grade H alloy steel is listed in the following table.
Element |
Content (%) |
Iron, Fe |
97 |
Nickel, Ni |
0.85 |
Manganese, Mn |
0.8 |
Molybdenum, Mo |
0.5 |
Chromium, Cr |
0.48 |
Copper, Cu |
0.33 |
Silicon, Si |
0.25 |
Carbon, C |
0.10 - 0.20 |
Vanadium, V |
0.06 |
Boron, B |
0.003 |
Physical Properties
The following table shows the physical properties of AISI A514 grade H alloy steel.
Properties |
Metric |
Imperial |
Density |
7.7 – 8.03 g/cm3 |
0.278 – 0.290 lb/in³ |
Mechanical Properties
The mechanical properties of AISI A514 grade H alloy steel are outlined in the following table.
Properties |
Metric |
Imperial |
Tensile strength, ultimate |
760 - 895 MPa |
110000 - 130000 psi |
Tensile strength, yield (@0.200%) |
690 MPa |
100000 psi |
Bulk modulus (typical for steel) |
140 GPa |
20300 ksi |
Shear modulus (typical for steel) |
80.0 GPa |
11600 ksi |
Elastic modulus |
190-210 GPa |
27557-30458 ksi |
Poisson's ratio |
0.27-0.30 |
0.27-0.30 |
Elongation at break (in 50 mm) |
18% |
18% |
Hardness, Brinell (@9.50 mm/0.374 in, for plates) |
235 - 293 |
235 - 293 |
Hardness, Knoop (converted from Brinell hardness) |
289 |
289 |
Hardness, Rockwell B (converted from Brinell hardness) |
98 |
98 |
Hardness, Rockwell C (converted from Brinell hardness) |
26 |
26 |
Hardness, Vickers (converted from Brinell hardness) |
278 |
278 |
Other Designations
Other designations that are equivalent to AISI A514 grade H alloy steel include the following:
- ASTM A514 (F)
- ASTM A517 (F)
- ASTM A592 (F)