Nov 16 2012
UNS C14530 has a copper content of not less than 99.90% copper.
The following table shows the mechanical properties of UNS C14530 flat products as a function of heat treatment and thickness.
|
Temper |
Thickness |
Tensile Str. |
Elong. |
|
H01 |
0.08mm. (0.003in.) |
276MPa (40ksi) |
5% |
|
|
0.51mm. (0.02 in.) |
276MPa (40ksi) |
23% |
|
H02 |
0.08mm. (0.003in.) |
310MPa (45ksi) |
12% |
|
|
0.51mm. (0.02 in.) |
310MPa (45ksi) |
12% |
|
H03 |
0.08mm. (0.003in.) |
- |
2% |
|
|
0.08mm. (0.003in.) |
331MPa (48ksi) |
- |
|
|
0.51mm. (0.02 in.) |
331MPa (48ksi) |
6% |
|
H04 |
0.08mm. (0.003in.) |
352MPa (51ksi) |
1% |
|
|
0.51mm. (0.02 in.) |
352MPa (51ksi) |
3% |
|
H06 |
0.08mm. (0.003in.) |
379MPa (55ksi) |
1% |
|
|
0.51mm. (0.02 in.) |
379MPa (55ksi) |
2% |
|
H08 |
0.08mm. (0.003in.) |
407MPa (59ksi) |
0% |
|
|
0.51mm. (0.02 in.) |
407MPa (59ksi) |
1% |
|
H10 |
0.08mm. (0.003in.) |
- |
0% |
|
|
0.08mm. (0.003in.) |
407MPa (59ksi) |
- |
|
|
0.51mm. (0.02 in.) |
- |
1% |
|
|
0.51mm. (0.02 in.) |
407MPa (59ksi) |
- |
|
OS015 |
0.08mm. (0.003in.) |
228MPa (33ksi) |
15% |
|
|
0.51mm. (0.02 in.) |
228MPa (33ksi) |
40% |
Equivalent materials to UNS C14530 copper alloy are ASTM B888 and B152.