Phosphorus-deoxidized UNS C13150 copper alloy has a copper content of not less than 99.5%.
The following table outlines the mechanical properties of UNS C13150 flat products as a function of heat treatment.
Temper |
Tensile Str. |
Yield Str. |
Rockwell |
B |
C |
F |
30T |
H00 |
220 MPa (32 ksi) |
140 MPa (20 ksi) |
- |
- |
54 |
- |
|
275 MPa (40 ksi) |
- |
- |
- |
82 |
- |
H01 |
290 MPa (42 ksi) |
- |
- |
- |
84 |
- |
|
235 MPa (34 ksi) |
193 MPa (28 ksi) |
- |
- |
60 |
- |
H02 |
316 MPa (46 ksi) |
- |
- |
- |
89 |
- |
|
253 MPa (37 ksi) |
210 MPa (360ksi) |
- |
- |
77 |
- |
H03 |
346 MPa (50 ksi) |
- |
- |
- |
91 |
- |
H03 |
283 MPa (41 ksi) |
210 MPa (32 ksi) |
- |
- |
82 |
- |
H04 |
295 MPa (43 ksi) |
243 MPa (35 ksi) |
- |
- |
86 |
- |
|
358 MPa (52 ksi) |
- |
- |
- |
93 |
- |
O60 |
204 MPa (30 ksi) |
- |
- |
- |
- |
- |
O60 |
261 MPa (38 ksi) |
- |
- |
- |
- |
- |