Phosphorus-deoxidized UNS C12500 has a copper content of not less than 99.88%.
The following table outlines the mechanical properties of UNS C12500 flat products as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
Shear Str |
Fatigue Str. |
B |
C |
F |
30T |
H00 |
1 mm (0.04 in) |
248 MPa (36 ksi) |
193 MPa (28 ksi) |
30% |
10 |
- |
60 |
25 |
172 MPa (25 ksi) |
- |
H01 |
0.076 mm (0.003 in) |
276 MPa (40 ksi) |
- |
5% |
- |
- |
- |
- |
- |
- |
0.5 mm (0.02 in) |
276 MPa (40 ksi) |
- |
23% |
- |
- |
- |
- |
- |
- |
H02 |
0.5 mm (0.02 in) |
310 MPa (45 ksi) |
- |
12% |
- |
- |
- |
- |
- |
- |
1 mm (0.04 in) |
290 MPa (42 ksi) |
248 MPa (36 ksi) |
14% |
40 |
- |
84 |
|
50 |
179 MPa (26 ksi) |
- |
H03 |
0.5 mm (0.02 in) |
331 MPa (48 ksi) |
- |
6% |
|
- |
- |
- |
- |
- |
H04 |
0.5 mm (0.02 in) |
352 MPa (51 ksi) |
- |
3% |
- |
- |
- |
- |
- |
- |
1 mm (0.04 in) |
345 MPa (50 ksi) |
310 MPa (45 ksi) |
6% |
50 |
- |
90 |
57 |
193 MPa (28 ksi) |
- |
H06 |
0.076 mm (0.003 in) |
379 MPa (55 ksi) |
- |
1% |
- |
- |
- |
- |
- |
- |
0.5 mm (0.02 in) |
379 MPa (55 ksi) |
|
2% |
- |
- |
- |
- |
- |
- |
H08 |
0.076 mm (0.003 in) |
407 MPa (59 ksi) |
- |
- |
- |
- |
- |
- |
- |
- |
0.5 mm (0.02 in) |
407 MPa (59 ksi) |
- |
1% |
- |
- |
- |
- |
- |
- |
1 mm (0.04 in) |
379 MPa (55 ksi) |
- |
1% |
- |
- |
- |
- |
- |
- |
H10 |
0.076 mm (0.003 in) |
407 MPa (59 ksi) |
- |
- |
- |
- |
- |
- |
- |
- |
0.5 mm (0.02 in) |
407 MPa (59 ksi) |
- |
1% |
- |
- |
- |
- |
- |
- |
1 mm (0.04 in) |
393 MPa (57 ksi) |
365 MPa (53 ksi) |
4% |
62 |
- |
95 |
64 |
- |
- |
M20 |
1mm (0.04 in) |
234 MPa (34 ksi) |
69 MPa (10 ksi |
45% |
- |
- |
45 |
|
159 MPa (23ksi) |
- |
OS015 |
0.076 mm (0.003 in) |
227 MPa (33 ksi) |
- |
15% |
- |
- |
- |
- |
- |
- |
0.5 mm (0.02 in) |
228 MPa (33 ksi) |
- |
40% |
- |
- |
- |
- |
- |
- |
OS025 |
1mm (0.04 in) |
234 MPa (34 ksi) |
76 MPa (11 ksi) |
45% |
- |
- |
45 |
|
159 MPa (23ksi) |
76 MPa (11 ksi) |