Nov 26 2012
Copper UNS C19170 has a copper content of not less than 96.8%.
The following table shows the mechanical properties of UNS C19170 flat products as a function of heat treatment.
| Temper |
Tensile Str. |
Elong. |
| H02 |
440MPa (64ksi) |
- |
|
480MPa (70ksi) |
7% |
|
520MPa (75ksi) |
- |
| H04 |
490MPa (71ksi) |
- |
|
540MPa (78ksi) |
5% |
|
560MPa (81ksi) |
- |
| H08 |
560MPa (81ksi) |
- |
|
600MPa (87ksi) |
5% |
|
640MPa (93ksi) |
- |
| H10 |
610MPa (88ksi) |
- |
|
680MPa (99ksi) |
5% |
|
730MPa (106ksi) |
- |
The chemical composition of UNS C19170 copper alloy is outlined in the following table.
| Element |
Content (%) |
| Copper, Cu |
96.8 min |
| Zinc, Zn |
1 |
| Tin, Sn |
0.8 |
| Nickel, Ni |
0.5-1 |
| Phosphorous, P |
0.08-0.2 |
| Iron, Fe |
0.05-0.15 |
| Lead, Pb |
0.02 |
| Silicon, Si |
0.01 |