Sep 27 2012
Commercial bronze UNS C22000 has a copper content of not less than 90%.
Tabulated below are the mechanical properties of UNS C22000 flat products as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
Shear Str. |
Fatigue Str. |
B |
C |
F |
30T |
H01 |
1mm (0.04 in) |
310MPa (45ksi) |
241 MPa (35ksi) |
25% |
42 |
- |
- |
44 |
228 MPa (33 ksi) |
- |
H02 |
1mm (0.04 in) |
359MPa (52ksi) |
310Mpa (45ksi) |
11% |
58 |
- |
- |
56 |
241 MPa (35ksi) |
- |
|
6.35 mm (0.25 in) |
359MPa (52ksi) |
310Mpa (45ksi) |
15% |
58 |
- |
- |
- |
241 MPa (35ksi) |
- |
H04 |
1mm (0.04 in) |
421MPa (61ksi) |
372MPa (54ksi) |
5% |
70 |
- |
- |
63 |
262MPa (38ksi) |
- |
H06 |
1mm (0.04 in) |
462MPa (67ksi) |
400MPa (58ksi) |
4% |
75 |
- |
- |
67 |
276MPa (40ksi) |
- |
H08 |
1mm (0.04 in) |
496MPa (73ksi) |
427MPa (62ksi) |
3% |
78 |
- |
- |
69 |
290MPa (42ksi) |
- |
M20 |
1mm (0.04 in) |
269MPa (39ksi) |
97MPa (14ksi) |
44% |
- |
- |
60 |
- |
214MPa (31ksi) |
- |
|
6.35 mm (0.25 in) |
255MPa (37ksi) |
69MPa (10ksi) |
45% |
- |
- |
53 |
28 |
- |
- |
OS015 |
1mm (0.04 in) |
283MPa (41ksi) |
103MPa (15ksi) |
42% |
- |
- |
65 |
26 |
221MPa (32ksi) |
- |
OS025 |
1mm (0.04 in) |
269MPa (39ksi) |
97MPa (14ksi) |
44% |
- |
- |
60 |
16 |
214MPa (31ksi) |
- |
OS035 |
1mm (0.04 in) |
262MPa (38ksi) |
83MPa (12ksi) |
45% |
- |
- |
57 |
12 |
207MPa (30ksi) |
- |
|
6.35 mm (0.25 in) |
262MPa (38ksi) |
83MPa (12ksi) |
50% |
- |
- |
57 |
- |
207MPa (30ksi) |
- |
OS050 |
1mm (0.04 in) |
255MPa (37ksi) |
69MPa (10ksi) |
45% |
- |
- |
53 |
6 |
193MPa (28ksi) |
- |
The chemical composition of UNS C22000 copper alloy is outlined in the following table.
Elements |
Content (%) |
Copper, Cu |
89.0-91.0 |
Iron, Fe |
0.05 |
Lead, Pb |
0.05 |
Zinc, Zn |
Balance |
Equivalent materials to UNS C22000 copper alloy are given in the table below.
ASTM B130 |
ASTM B131 |
ASTM B134 |
ASTM B135 |
ASTM B372 |
ASTM B587 |
ASTM B694 |
MIL B-18907 |
MIL C-3383 |
MIL B-20292 |
MIL W-6712 |
MIL W-85 |
QQ W321 |
SAE J461 |
SAE J463 |
ASTM B36 |
|
|
|
|