UNS C44250 copper alloy has a copper content of no less than 73%.
The following table shows the mechanical properties of UNS C44250 flat products as a function of heat treatment.
Temper |
Tensile Str. |
Elong. |
H01 |
500 MPa (73 ksi) |
- |
|
430 MPa (62 ksi) |
20% |
H02 |
540 MPa (78 ksi) |
- |
|
470 MPa (68 ksi) |
15% |
H03 |
530 MPa (77 ksi) |
8% |
|
610 MPa (88 ksi) |
- |
H04 |
600 MPa (87 ksi) |
5% |
|
680 MPa (99 ksi) |
- |
H06 |
670 MPa (97 ksi) |
- |
|
770 MPa (112 ksi) |
- |
H08 |
810 MPa (117 ksi) |
- |
|
730 MPa (106 ksi) |
- |
H10 |
780 MPa (113 ksi) |
- |
|
870 MPa (126 ksi) |
- |
H12 |
820 MPa (119 ksi) |
- |
|
900 MPa (130 ksi) |
- |
The chemical composition of UNS C44250 copper alloy is outlined in the following table.
Element |
Content (%) |
Copper, Cu |
73-76 |
Tin, Sn |
0.50-1.5 |
Iron, Fe |
0.2 |
Nickel, Ni |
0.2 |
Phosphorous, P |
0.1 |
Lead, Pb |
0.07 |
Zinc, Zn |
Remainder |