UNS C65100 low-silicon bronze B alloy has a copper content of not less than 98.5%.
The following table shows the mechanical properties of UNS C65100 tubes as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
B |
C |
F |
30T |
OS015 |
1.8 mm (0.065 in) |
310 MPa (45 ksi) |
138 MPa (20 ksi) |
55% |
- |
- |
68 |
- |
The chemical composition of UNS C65100 copper alloy is outlined in the following table.
Element |
Content (%) |
Zinc, Zn |
1.5 |
Silicon, Si |
0.8-2.0 |
Iron, Fe |
0.8 |
Manganese, Mn |
0.7 |
Lead, Pb |
0.05 |
Copper, Cu |
Remainder |
Equivalent materials to UNS C65100 copper alloy are:
- ASME SB315
- ASME SB98
- ASTM B105
- ASTM B315
- ASTM B432
- ASTM B96
- ASTM B98
- ASTM B99
- ASTM F467
- ASTM F468