Dec 13 2012
UNS C65100 low-silicon bronze B alloy has a copper content of not less than 98.5%.
The following table shows the mechanical properties of UNS C65100 wires as a function of heat treatment and thickness.
|
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Shear Str. |
Fatigue Str. |
|
H00 |
2 mm (0.08 in) |
379 MPa (55 ksi) |
276 MPa (40 ksi) |
40% |
248 MPa (36 ksi) |
- |
|
H01 |
2 mm (0.08 in) |
448 MPa (65 ksi) |
345 MPa (50 ksi) |
25% |
276 MPa (40 ksi) |
- |
|
H02 |
2 mm (0.08 in) |
552 MPa (80 ksi) |
434 MPa (63 ksi) |
11% |
345 MPa (50 ksi) |
172 MPa (25 ksi) |
|
H04 |
2 mm (0.08 in) |
689 MPa (100 ksi) |
483 MPa (70 ksi) |
11% |
345 MPa (50 ksi) |
172 MPa (25 ksi) |
|
H06 |
2 mm (0.08 in) |
172 MPa (105 ksi) |
490 MPa (71 ksi) |
10% |
365 MPa (53 ksi) |
193 MPa (28 ksi) |
The chemical composition of UNS C65100 copper alloy is outlined in the following table.
|
Element |
Content (%) |
|
Zinc, Zn |
1.5 |
|
Silicon, Si |
0.8-2.0 |
|
Iron, Fe |
0.8 |
|
Manganese, Mn |
0.7 |
|
Lead, Pb |
0.05 |
|
Copper, Cu |
Remainder |
Equivalent materials to UNS C65100 copper alloy are:
-
ASME SB315
-
ASME SB98
-
ASTM B105
-
ASTM B315
-
ASTM B432
-
ASTM B96
-
ASTM B98
-
ASTM B99
-
ASTM F467
-
ASTM F468