Super alloys have an ability to function in environments with high temperatures and severe mechanical stressing, and also where high surface stability is required. They can be strengthened by solid-solution hardening, work hardening, and precipitation hardening. They are found in different shapes. Cobalt-based, iron-based, and nickel-based are the three groups of super alloys.
Hastelloy (r) D-205™ has good corrosion resistance and formability. The following datasheet gives more details about Hastelloy (r) D-205™.
Chemical Composition
The following table shows the chemical composition of Hastelloy (r) D-205™.
Element |
Content (%) |
Nickel, Ni |
64.47-64.5 |
Chromium, Cr |
20 |
Iron, Fe |
6 |
Silicon, Si |
5 |
Molybdenum, Mo |
2.5 |
Copper, Cu |
2 |
Carbon, C |
0.030 |
Mechanical Properties
The mechanical properties of Hastelloy (r) D-205™ are outlined in the following table.
Properties |
Metric |
Imperial |
Tensile strength (mill annealed) |
786 MPa |
114000 psi |
Tensile strength (aged 24 hrs/1000°F) |
979 MPa |
142000 psi |
Yield strength (@ strain 0.200%, mill annealed) |
338 MPa |
49000 psi |
Elongation at break (in 2in., aged 24hrs/1000°F) |
28.60% |
28.60% |
Elongation at break (in 2in., mill annealed) |
56.50% |
56.50% |