Beryllium Oxide - Beryllia

Material: Beryllium Oxide - Beryllia
Composition: blank
Property Minimum Value (S.I.) Maximum Value (S.I.) Units (S.I.) Minimum Value (Imp.) Maximum Value (Imp.) Units (Imp.)
Atomic Volume (average) 0.0043 0.0045 m3/kmol 262.402 274.607 in3/kmol
Density 2.8 3.01 Mg/m3 174.798 187.908 lb/ft3
Energy Content 200 300 MJ/kg 21667.7 32501.6 kcal/lb
Bulk Modulus 276 333.3 GPa 40.0304 48.341 106 psi
Compressive Strength 785 2800 MPa 113.855 406.106 ksi
Ductility 0.00032 0.00082 0.00032 0.00082 NULL
Elastic Limit 79 306 MPa 11.458 44.3815 ksi
Endurance Limit 70 276 MPa 10.1526 40.0304 ksi
Fracture Toughness 1 2.5 MPa.m1/2 0.910047 2.27512 ksi.in1/2
Hardness 5500 13000 MPa 797.708 1885.49 ksi
Loss Coefficient 1e-005 3e-005 1e-005 3e-005 NULL
Modulus of Rupture 172 368 MPa 24.9465 53.3739 ksi
Poisson's Ratio 0.26 0.34 0.26 0.34 NULL
Shear Modulus 130.76 153.8 GPa 18.9651 22.3068 106 psi
Tensile Strength 79 306 MPa 11.458 44.3815 ksi
Young's Modulus 331.7 400 GPa 48.109 58.0151 106 psi
Glass Temperature K °F
Latent Heat of Fusion 1520 1930 kJ/kg 653.479 829.746 BTU/lb
Maximum Service Temperature 1073 2318 K 1471.73 3712.73 °F
Melting Point 2787 2899 K 4556.93 4758.53 °F
Minimum Service Temperature 0 0 K -459.67 -459.67 °F
Specific Heat 750 1020 J/kg.K 0.580394 0.789335 BTU/lb.F
Thermal Conductivity 209 330 W/m.K 391.255 617.771 BTU.ft/h.ft2.F
Thermal Expansion 7.4 8.9 10-6/K 13.32 16.02 10-6/°F
Breakdown Potential 27 31 MV/m 685.8 787.4 V/mil
Dielectric Constant 6.1 7.5 6.1 7.5 NULL
Resistivity 1e+020 1e+023 10-8 ohm.m 1e+020 1e+023 10-8 ohm.m
Environmental Properties
  Resistance Factors
1=Poor 5=Excellent
Flammability 5
Fresh Water 5
Organic Solvents 5
Oxidation at 500C 5
Sea Water 5
Strong Acid 4
Strong Alkalis 4
UV 5
Wear 5
Weak Acid 5
Weak Alkalis 5

This data is provided subject to AZoM.com's terms and conditions. Data reproduced with permission of Granta Design Limited www.grantadesign.com and Ceram Research Limited www.ceram.co.uk

Sponsored Content

Editorial Highlights

The Current State of the Global Semiconductor Market

The Current State of the Global Semiconductor Market

The global semiconductor market has entered an exciting period. Demand for chip technology is both driving the industry as well as hindering it, with current chip shortages predicted to last for some time. Current trends will likely shape the future of the industry, which is set to continue to show

How are Graphene Batteries Made?

How are Graphene Batteries Made?

The primary distinction between graphene-based batteries and solid-state batteries lies in the composition of either electrode. Although the cathode is commonly changed, carbon allotropes can also be employed in fabricating anodes.

Terms

While we only use edited and approved content for Azthena answers, it may on occasions provide incorrect responses. Please confirm any data provided with the related suppliers or authors. We do not provide medical advice, if you search for medical information you must always consult a medical professional before acting on any information provided.

Your questions, but not your email details will be shared with OpenAI and retained for 30 days in accordance with their privacy principles.

Please do not ask questions that use sensitive or confidential information.

Read the full Terms & Conditions.

Provide Feedback