Copper Centrifugal Cast Alloy (UNS C86700) - Mechanical Properties

UNS C86700 has a copper content of not less than 55%.

Tabulated below are the mechanical properties of UNS C86700 centrifugal cast alloy as a function of heat treatment.

Temper Tensile Str. Yield Str. Elong.
M02 552MPa (80ksi) 221MPa (32ksi) 15%

The chemical composition of UNS C86700 copper alloy is outlined in the following table.

Elements Content (%)
Copper, Cu 55.0-60.0
Zinc, Zn 30.0-38.0
Tin, Sn 1.5
Aluminum, Al 1.0-3.0
Iron, Fe 1.0-3.0
Nickel, Ni 1
Lead, Pb 0.50-1.5
Manganese, Mn 0.10-3.5

Equivalent materials to UNS C86700 copper alloy are given in the table below.

  • ASTM B271
  • ASTM B30
  • ASTM B584
  • ASTM B763

Tell Us What You Think

Do you have a review, update or anything you would like to add to this article?

Leave your feedback
Your comment type
Submit

While we only use edited and approved content for Azthena answers, it may on occasions provide incorrect responses. Please confirm any data provided with the related suppliers or authors. We do not provide medical advice, if you search for medical information you must always consult a medical professional before acting on any information provided.

Your questions, but not your email details will be shared with OpenAI and retained for 30 days in accordance with their privacy principles.

Please do not ask questions that use sensitive or confidential information.

Read the full Terms & Conditions.