UNS C19500 copper alloy has a copper content of not less than 96%.
The following table shows the mechanical properties of UNS C19500 flat products as a function of heat treatment and thickness.
| Temper |
Thickness |
Tensile Str. |
Elong. |
Fatigue Str. |
| TF00 |
1 mm (0.04 in) |
552 MPa (70 ksi) |
15% |
179 MPa (26 ksi) |
| TL02 |
1 mm (0.04 in) |
552 MPa (80 ksi) |
10% |
- |
| TL08 |
1 mm (0.04 in) |
641 MPa (93 ksi) |
4% |
200 MPa (29 ksi) |
| TL10 |
1 mm (0.04 in) |
669 MPa (97ksi) |
2% |
- |
The chemical composition of UNS C19500 copper alloy is outlined in the following table.
| Element |
Content (%) |
| Copper, Cu |
96 |
| Iron, Fe |
1.0-2.0 |
| Cobalt, Co |
0.30-1.3 |
| Zinc, Zn |
0.2 |
| Tin, Sn |
0.10-1.0 |
| Aluminum, Al |
0.02 |
| Phosphorous, P |
0.01-.35 |
Equivalent materials to UNS C19500 copper alloy carbon steel are ASTM B465.