Sep 27 2012
Copper UNS C51100 has a copper content of not less than 95.6%.
The following table shows the mechanical properties of UNS C51100 flat products as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
B |
C |
F |
30T |
H01 |
1mm (0.04in) |
379MPa (55ksi) |
345MPa (50ksi) |
36% |
48 |
- |
- |
45 |
H02 |
1mm (0.04in) |
1144MPa (166ksi) |
372MPa (54ksi) |
34% |
70 |
- |
- |
65 |
H03 |
1mm (0.04in) |
510MPa (74ksi) |
- |
11% |
84 |
- |
- |
72 |
H04 |
1mm (0.04in) |
552MPa (80ksi) |
510MPa (74ksi) |
8% |
86 |
- |
- |
74 |
H06 |
1mm (0.04in) |
634MPa (92ksi) |
- |
4% |
91 |
- |
- |
78 |
H08 |
1mm (0.04in) |
710MPa (103ksi) |
552MPa (80ksi) |
1% |
93 |
- |
- |
79 |
H10 |
1mm (0.04in) |
710MPa (103ksi) |
552MPa (80ksi) |
2% |
95 |
|
|
80 |
HR02 |
- |
434MPa (63ksi) |
- |
26% |
- |
- |
- |
- |
HR04 |
- |
552MPa (80ksi) |
- |
15% |
- |
- |
- |
- |
HR06 |
- |
634MPa (92ksi) |
- |
10% |
- |
- |
- |
- |
HR08 |
- |
676MPa (98ksi) |
- |
8% |
- |
- |
- |
- |
OS015 |
1mm (0.04in) |
338MPa (49ksi) |
- |
50% |
- |
- |
76 |
- |
OS025 |
1mm (0.04in) |
345MPa (50ksi) |
- |
46% |
- |
- |
75 |
- |
OS035 |
1mm (0.04in) |
331MPa (48ksi) |
- |
47% |
- |
- |
73 |
- |
OS050 |
1mm (0.04in) |
317MPa (46ksi) |
- |
48% |
- |
- |
70 |
- |
Equivalent materials to UNS C51100 copper alloy are the following:
The chemical composition of UNS C51100 copper alloy is outlined in the following table.
Element |
Content (%) |
Tin, Sn |
3.5-4.9 |
Zinc, Zn |
0.3 |
Iron, Fe |
0.1 |
Phosphorous, P |
0.03-0.35 |
Lead, Pb |
0.05 |
Copper, Cu |
Balance |