Introduction
Magnesium alloys are light in weight, and have high strength and good vibration damping characteristics.
The following datasheet gives an overview of magnesium K1A-F alloy.
Chemical Composition
The following table shows the chemical composition of magnesium K1A-F alloy.
Element |
Content (%) |
Magnesium, Mg |
99 |
Zirconium, Zr |
0.40 - 1 |
Physical Properties
The physical properties of magnesium K1A-F alloy are given in the following table.
Properties |
Metric |
Imperial |
Density |
1.74 g/cm³ |
0.0629 lb/in³ |
Mechanical Properties
The mechanical properties of extruded magnesium K1A-F alloy are listed in the following table.
Properties |
Metric |
Imperial |
Tensile strength |
180 MPa |
26100 psi |
Yield strength (@ strain 0.200%) |
55 MPa |
7980 psi |
Compressive yield strength (at 0.2% offset) |
55 MPa |
7980 psi |
Ultimate bearing strength |
317 MPa |
46000 psi |
Bearing yield strength |
125 MPa |
18100 psi |
Shear strength |
55 MPa |
7980 psi |
Shear modulus (typical for steel) |
17 GPa |
2470 ksi |
Elastic modulus |
44.8 GPa |
6498 ksi |
Elongation at break (in 50 mm) |
19% |
19% |
Machinability (relative rating, 100=best) |
100 |
100 |
Thermal Properties
The following table outlines the thermal properties of magnesium K1A-F alloy.
Properties |
Metric |
Imperial |
Thermal expansion co-efficient (@ 0-100°C/32-212°F) |
27 µm/m°C |
15 µin/in°F |
Thermal conductivity |
122 W/mK |
847 BTU in/hr.ft².°F |
Other Designations
Other designation that is equivalent to magnesium K1A-F alloy includes ASTM B 80.