Super Alloy Nimonic PE11™

Topics Covered

Introduction
Chemical Composition
Physical Properties
Mechanical Properties
Fabrication and Heat Treatment
     Machinability
     Forming
     Welding
     Heat Treatment
     Forging
     Hot Working
     Cold Working
     Annealing
Applications

Introduction

Super alloys or high performance alloys contain a number of elements in a variety of combinations to reach a desired result. These alloys are excellent to use at high temperatures and severe mechanical stress, and also in cases where high surface stability is needed. Super alloys provide good creep and oxidation resistance.

Strengthening of super alloys is performed by work hardening, solid-solution hardening, and precipitation hardening methods.

Nimonic PE11™ belongs to the nickel-chromium-molybdenum group of alloys. It has higher iron content. It can be hardened by heat treatment.

The following datasheet will provide more details about Nimonic PE11™.

Chemical Composition

The following table shows the chemical composition of Nimonic PE11™.

Element Content (%)
Nickel, Ni 37-41
Iron, Fe 32
Chromium, Cr 17-19
Molybdenum, Mo 4.75-5.75
Titanium, Ti 2.20-2.50
Cobalt, Co  1
Aluminum, Al 0.70-1.0
Silicon, Si  0.50
Copper, Cu  0.50
Manganese, Mn  0.20
Carbon, C 0.030-0.080
Zirconium, Zr 0.020-0.050
Sulfur, S  0.015
Boron, B  0.0010

Physical Properties

The physical properties of Nimonic PE11™ are outlined in the following table.

Properties Metric Imperial
Density 8.02 g/cm³ 0.290 lb/in³
Melting point 1280-1350°C 2340-2460°F

Mechanical Properties

The mechanical properties of Nimonic PE11™ are provided below.

Properties Metric Imperial
Tensile strength (precipitation hardened, value at room temperature) 1060 MPa 154000 psi
Yield strength (@strain 0.200%, precipitation hardened, value at room temperature) 700 MPa 102000 psi
Elongation at break (precipitation hardened) 20% 20%

Fabrication and Heat Treatment

Machinability

Traditional machining methods that are used for iron-based alloys can be used for Nimonic PE11™. This alloy can be work-hardened during machining. Before cutting is performed, it is recommended that heavy duty machining equipment and tooling be used so as to reduce chatter or work-hardening of the alloy. During high speed operations such as grinding, turning, or milling, water-base coolants are preferred. The use of heavy lubricants while drilling, tapping, broaching or boring is recommended.

Forming

Nimonic PE11™ has good ductility and can be easily formed using all the conventional methods. This alloy is stronger than regular steel; hence it requires a more powerful equipment to complete the forming process. It is recommended that heavy-duty lubricants should be used while cold forming. At the end of this process, all traces of lubricant has to be cleaned off to prevent embrittlement.

Welding

Nimonic PE11™ can be welded using the traditional welding methods. Some of the commonly used methods are shielded metal-arc welding, gas metal-arc welding, submerged-arc welding, and gas-tungsten arc welding. It is recommended that matching alloy filler metal should be used. Before the welding process begins, the surface to be welded should be cleaned and should be free from oil, paint or crayon stains.

Heat Treatment

Nimonic PE11™ has to be solution annealed at 1021°C (1870°F) for 2 h and then air cooled. This process is repeated twice at 799°C (1470°F) for 2 h and air cooled, and at 699°C (1290°F) for 16 h and air cooled.

Forging

Nimonic PE11™ can be forged at 1176-968°C (2150-1775°F).

Hot Working

Nimonic PE11™ can be hot worked at 1176-954°C (2150-1750°F).

Cold Working

Cold working can be performed using standard tooling. It is better to avoid using plain carbon tool steels for forming as they cause galling. To minimize galling and provide a neat finish, soft die materials containing bronze and zinc alloys are recommended. However, the life of the die is short. Likewise, heavy duty lubricants should be used to reduce galling in all forming operations.

Annealing

Nimonic PE11™ can be solution annealed at 1021°C (1870°F) for 2 h and then air cooled.

Applications

Nimonic PE11™ is mainly used in high temperature oxidizing applications, especially in cases where strength at temperature is a primary requirement, e.g. industrial furnace components or gas turbine hot sections.

Tell Us What You Think

Do you have a review, update or anything you would like to add to this article?

Leave your feedback
Your comment type
Submit

While we only use edited and approved content for Azthena answers, it may on occasions provide incorrect responses. Please confirm any data provided with the related suppliers or authors. We do not provide medical advice, if you search for medical information you must always consult a medical professional before acting on any information provided.

Your questions, but not your email details will be shared with OpenAI and retained for 30 days in accordance with their privacy principles.

Please do not ask questions that use sensitive or confidential information.

Read the full Terms & Conditions.