Sep 27 2012
UNS C10910 has a copper content of not less than 99.95% copper.
The following table shows the mechanical properties of UNS C10910 flat products as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
Shear Str. |
Fatigue Str. |
B |
C |
F |
30T |
H00 |
1mm. (0.04 in.) |
248MPa (36ksi) |
193MPa (28ksi) |
30% |
10 |
- |
60 |
25 |
172MPa (25ksi) |
- |
|
6.4mm. (0.25 in.) |
248MPa (36ksi) |
193MPa (28ksi) |
40% |
10 |
- |
60 |
64 |
172MPa (25ksi) |
76MPa (11ksi) |
H01 |
1mm. (0.04 in.) |
262MPa (38ksi) |
207MPa (30ksi) |
25% |
25 |
- |
70 |
36 |
172MPa (25ksi) |
- |
|
6.4mm. (0.25 in.) |
262MPa (38ksi) |
207MPa (30ksi) |
35% |
25 |
- |
70 |
64 |
172MPa (25ksi) |
76MPa (11ksi) |
H02 |
1mm. (0.04 in.) |
290MPa (42ksi) |
248MPa (36ksi) |
14% |
40 |
- |
84 |
50 |
179MPa (26ksi) |
90MPa (13ksi) |
H04 |
1mm. (0.04 in.) |
345MPa (50ksi) |
310MPa (45ksi) |
6% |
50 |
- |
90 |
57 |
193MPa (28ksi) |
90MPa (13ksi) |
|
6.4mm. (0.25 in.) |
524MPa (100ksi) |
414MPa (90ksi) |
70% (24%) |
50% (100%) |
- |
140 (180) |
128 |
344MPa (56ksi) |
152MPa (22ksi) |
|
25.4mm. (1 in.) |
310MPa (45ksi) |
276MPa (40ksi) |
20% |
45 |
- |
85 |
64 |
179MPa (26ksi) |
76MPa (11ksi) |
H08 |
1mm. (0.04 in.) |
379MPA (55ksi) |
345MPa (50ksi) |
4% |
60 |
- |
94 |
63 |
200MPa (29ksi) |
97MPa (14ksi) |
H10 |
1mm. (0.04 in.) |
20393MPa (57ksi) |
365MPa (53ksi) |
4% |
62 |
- |
95 |
64 |
200MPa (29ksi) |
97MPa (14ksi) |
M20 |
1mm. (0.04 in.) |
234MPa (34ksi) |
69MPa |
45% |
62 |
- |
45 |
64 |
159MPa (23ksi) |
97MPa (14ksi) |
|
6.4mm. (0.25 in.) |
221MPa (32ksi) |
69MPa |
50% |
50 |
- |
40 |
64 |
152MPa (22ksi) |
76MPa (11ksi) |
OS025 |
1mm. (0.04 in.) |
234MPa (34ksi) |
76MPa (11ksi) |
45% |
62 |
- |
45 |
64 |
159MPa (23ksi) |
76MPa (11ksi) |
OS050 |
1mm. (0.04 in.) |
221MPa (32ksi) |
69MPa (10ksi) |
45% |
62 |
- |
45 |
64 |
152MPa (22ksi) |
76MPa (11ksi) |
|
6.4mm. (0.25 in.) |
221MPa (32ksi) |
69MPa (10ksi) |
50% |
50 |
- |
40 |
64 |
152MPa (22ksi) |
76MPa (11ksi) |
Equivalent material to UNS C10910 copper alloy is ASTM B152.