UNS C14500 tellurium-bearing copper alloy has a copper content of not less than 99.5%.
The following table outlines the mechanical properties of UNS C14500 tubes as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Shear Str. |
H00 |
2 mm (0.08 in) |
262 MPa (38 ksi) |
207 Mpa (30 ksi) |
20% |
172 MPa (25 ksi) |
H02 |
2 mm (0.08 in) |
352 MPa (51 ksi) |
283 MPa (41 ksi) |
6% |
186 MPa (27 ksi) |
H04 |
2 mm (0.08 in) |
386 MPa (55 ksi) |
352 MPa (51 ksi) |
3% |
207 MPa (30 ksi) |
OS035 |
2 mm (0.08 in) |
228 MPa (33 ksi) |
76 MPa (11 ksi) |
40% |
152 MPa (22 ksi) |
Equivalent materials to UNS C14500 copper alloy include:
- ASME B16.22
- ASTM B124
- ASTM B216
- ASTM B224
- ASTM B283
- ASTM B301
- ASTM B442
- ASTM B5
- ASTM B623
- SAE J462
- SAE J463