Tellurium-Bearing UNS C14510 has a copper content of not less than 99.85%.
Tabulated below are the mechanical properties of UNS C14510 wires as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
Shear Str. |
B |
C |
F |
30T |
H00 |
2mm (0.08in) |
262MPa (38ksi) |
207MPa (30ksi) |
20% |
- |
- |
- |
- |
172MPa (25ksi) |
H02 |
2mm (0.08in) |
352MPa (51ksi) |
283MPa (41ksi) |
6% |
- |
- |
- |
- |
186MPa (27ksi) |
H04 |
2mm (0.08in) |
386MPa (56ksi) |
352MPa (51ksi) |
3% |
- |
- |
- |
- |
207MPa (30ksi) |
OS035 |
2mm (0.08in) |
288MPa (33ksi) |
76MPa (11ksi) |
40% |
- |
- |
- |
- |
152MPa (22ksi) |