UNS C10800 has a copper content of not less than 99.95% copper.
Tabulated below are the mechanical properties of UNS C10800 rods as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
Shear Str |
Fatigue Str. |
B |
C |
F |
30T |
H04 |
6.35mm (0.25in) |
379MPa (55ksi) |
345MPa (50ksi) |
20% |
60 |
- |
94 |
- |
200MPa (29ksi) |
- |
|
51mm (2in) |
310MPa (45ksi) |
276MPa (40ksi) |
20% |
45 |
- |
85 |
- |
176MPa (26ksi) |
- |
|
25.4mm (1in) |
331MPa (48ksi) |
303MPa (44ksi) |
16% |
47 |
- |
87 |
- |
186MPa (27ksi) |
117MPa (17ksi) |
Equivalent materials to UNS C10800 copper alloy are given in the table below.
ASTM B111 |
ASTM B133 |
ASTM B152 |
ASTM B224 |
ASTM B280 |
ASTM B302 |
ASTM B306 |
ASTM B359 |
ASTM B360 |
ASTM B379 |
ASTM B395 |
ASTM B42 |
ASTM B432 |
ASTM B447 |
ASTM B447 |
ASTM B543 |
ASTM B638 |
ASTM B640 |
ASTM B641 |
ASTM B68 |
ASTM B687 |
ASTM B698 |
ASTM B716 |
ASTM B743 |
ASTM B75 |
ASTM B88 |
MIL B-20292 |
MIL T-24107 |
|
|
|
|
|
|
|