Phosphorus-deoxidized UNS C12000 has a copper content of not less than 99.9%.
The following table shows the mechanical properties of UNS C12000 rods as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
Shear Str |
B |
C |
F |
30T |
M20 |
25.4 mm (1 in) |
221 MPa (32 ksi) |
69 MPa (10 ksi) |
55% |
- |
- |
40 |
- |
152 MPa (22 ksi) |
OS050 |
25.4 mm (1 in) |
221 MPa (32 ksi) |
69 MPa (10 ksi) |
55% |
- |
- |
40 |
- |
152 MPa (22 ksi) |
Equivalent materials to UNS C12000 copper alloy are included in the following table.
ASME SB111 |
ASTM B133 |
ASTM B302 |
ASTM B447 |
ASTM B641 |
ASTM B88 |
ASME SB133 |
ASTM B152 |
ASTM B306 |
ASTM B451 |
ASTM B68 |
MIL B-18907 |
ASME SB359 |
ASTM B187 |
ASTM B359 |
ASTM B5 |
ASTM B687 |
MIL B-20292 |
ASME SB395 |
ASTM B188 |
ASTM B372 |
ASTM B506 |
ASTM B698 |
MIL T-24107 |
ASME SB42 |
ASTM B224 |
ASTM B395 |
ASTM B623 |
ASTM B716 |
MIL T-3235 |
ASME SB75 |
ASTM B272 |
ASTM B42 |
ASTM B638 |
ASTM B743 |
MIL W-85 |
ASTM B111 |
ASTM B280 |
ASTM B442 |
ASTM B640 |
ASTM B75 |
SAE J461 |