Sep 27 2012
UNS C18150 copper alloy has a copper content of not less than 98.9%.
The following table shows the mechanical properties of UNS C18150 rods as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
B |
C |
F |
30T |
TL04 |
12.3 mm (0.485 in) |
558 MPa (81 ksi) |
545 MPa (79 ksi) |
14% |
82 |
- |
- |
- |
|
19.1 mm (0.75 in) |
545 MPa (79 ksi) |
517 MPa (75 ksi) |
16% |
78 |
- |
- |
- |
TL06 |
12.7 mm (0.50 in) |
586 MPa (85 ksi) |
579 MPa (84 ksi) |
16% |
82 |
- |
- |
- |
|
15.9 mm (0.625) |
565 MPa (82 ksi) |
538 MPa (78 ksi) |
14% |
82 |
- |
- |
- |
TX00 |
25.4 mm (1 in) |
548 MPa (65 ksi) |
379 MPa (55 ksi) |
13% |
75 |
- |
- |
- |
The chemical composition of UNS C18150 copper alloy is outlined in the following table.
Element |
Content (%) |
Copper, Cu |
98.9 |
Chromium, Cr |
1 |
Zirconium, Zr |
0.11 |