UNS C18150 copper alloy has a copper content of not less than 98.9%.
The following table shows the mechanical properties of UNS C18150 wires as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
B |
C |
F |
30T |
TL02 |
15.2 mm (0.60 in) |
469 MPa (68 ksi) |
400 MPa (58 ksi) |
19% |
75 |
- |
- |
- |
|
17.8 mm (0.70 in) |
469 MPa (69 ksi) |
238 MPa (49 ksi) |
15% |
76 |
- |
- |
- |
TL04 |
12.7 mm (0.50 in) |
469 MPa (68 ksi) |
455 MPa (66 ksi) |
15% |
73 |
- |
- |
- |
|
15.2 mm (0.60 in) |
469 MPa (68 ksi) |
434 MPa (63 ksi) |
20% |
74 |
- |
- |
- |
The chemical composition of UNS C18150 copper alloy is outlined in the following table.
Element |
Content (%) |
Copper, Cu |
98.9 |
Chromium, Cr |
1 |
Zirconium, Zr |
0.11 |