Sep 27 2012
Phosphorus-deoxidized UNS C14200 has a copper content of not less than 99.4%.
Tabulated below are the mechanical properties of UNS C14200 tubes as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
Shear Str. |
Fatigue Str. |
B |
C |
F |
30T |
OS025 |
1.65MPa (0.065in) |
234MPa (34ksi) |
76MPa (11ksi) |
45% |
- |
- |
45 |
- |
159MPa (23ksi) |
- |
OS050 |
1.65MPa (0.065in) |
221MPa (32ksi) |
69MPa (10ksi) |
45% |
- |
- |
40 |
- |
152MPa (22ksi) |
76MPa (11ksi) |
Equivalent materials to UNS C14200 copper alloy are given in the table below.
ASME SB111 |
ASME SB133 |
ASME SB359 |
ASME SB395 |
ASME SB75 |
ASTM B111 |
ASTM B133 |
ASTM B152 |
ASTM B216 |
ASTM B224 |
ASTM B359 |
ASTM B379 |
ASTM B395 |
ASTM B442 |
ASTM B447 |
ASTM B5 |
ASTM B623 |
ASTM B75 |
MIL T-24107 |
|
|
|
|
|
|