Dec 20 2012
Copper UNS C67600 has a copper content of not less than 57%.
The following table shows the mechanical properties of UNS C67600 rods as a function of heat treatment and thickness.
Temper |
Thickness |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
B |
C |
F |
30T |
H01 |
25.4mm (1in) |
531MPa (77ksi) |
310MPa (45ksi) |
- |
83 |
- |
- |
- |
|
25.4mm (1in) |
- |
- |
23% |
- |
- |
- |
- |
|
50.8mm (2in) |
496MPa (72ksi) |
290MPa (42ksi) |
- |
77 |
- |
- |
- |
|
50.8mm (2in) |
- |
- |
27% |
- |
- |
- |
- |
H02 |
25.4mm (1in) |
579MPa (84ksi) |
414MPa (60ksi) |
- |
90 |
- |
- |
- |
|
- |
- |
- |
19% |
- |
- |
- |
- |
O60 |
- |
448MPa (65ksi) |
207MPa (30ksi) |
- |
65 |
- |
- |
- |
|
- |
- |
- |
33% |
- |
- |
- |
- |
The chemical composition of UNS C67600 copper alloy is outlined in the following table.
Element |
Content (%) |
Copper, Cu |
57-60 |
Tin, Sn |
0.5-1.5 |
Lead, Pb |
0.5-1 |
Iron, Fe |
0.4-1.3 |
Manganese, Mn |
0.05-0.5 |
Zinc, Zn |
Remainder |