UNS C95300 has a copper content of not less than 86%.
Tabulated below are the mechanical properties of UNS C95300 sand cast alloy as a function of heat treatment.
Temper |
Tensile Str. |
Yield Str. |
Elong. |
Rockwell |
Shear Str. |
Fatigue Str. |
B |
C |
F |
30T |
M01 |
517MPa (75ksi) |
186MPa (27ksi) |
25% |
67 |
- |
- |
- |
283MPa (41ksi) |
152MPa (22ksi) |
|
448MPa (65ksi) |
172MPa (25ksi) |
20% |
- |
- |
- |
- |
- |
- |
TQ50 |
586MPa (85ksi) |
290MPa (42ksi) |
15% |
81 |
- |
- |
- |
317MPa (46ksi) |
186MPa (27ksi) |
|
550MPa (80ksi) |
275MPa (40ksi) |
12% |
- |
- |
- |
- |
- |
- |
The chemical composition of UNS C95300 copper alloy is outlined in the following table.
Elements |
Content (%) |
Copper, Cu |
86 |
Aluminum, Al |
9.0-11.0 |
Iron, Fe |
.8-1. |
Equivalent materials to UNS C95300 copper alloy are:
- ASTM B148
- ASTM B30
- ASTM B505
- ASTM B763
- ASTM B806
- MIL C-11866
- QQ C390
- SAE J461
- SAE J462