Introduction
The high silicon bronze UNS C65500 has moderate strength and good corrosion resistance. The conductivity of UNS C65500 is lesser than the conductivity of unalloyed copper. The pr operties and applications of UNS C65500 copper alloy are similar to that of the C64200.
The following datasheet provides the chemical composition and the properties of UNS C65500.
Chemical Composition
The chemical composition of UNS C65500 copper alloy is given in the following table.
Element |
Content (%) |
Cu |
97.0 |
Si |
3.0 |
Physical Properties
The following table gives the physical properties of UNS C65500.
Properties |
Metric |
Imperial |
Density |
8.8-8.94 g/cm3 |
0.317-0.323 lb/in³ |
Melting point |
971°C |
1780°F |
Mechanical Properties
The mechanical properties of UNS C65500 copper alloy are outlined in the following table.
Properties |
Metric |
Imperial |
Tensile strength |
Depending on temper |
Depending on temper |
Yield strength |
Depending on temper |
Depending on temper |
Poisson's ratio |
0.34 |
0.34 |
Elastic modulus |
117 GPa |
16969 ksi |
Other Designations
Equivalent designations to UNS C65500 include:
- ASME SB315
- ASME SB96
- ASME SB98
- ASTM B100
- ASTM B105
- ASTM B124
- ASTM B283
- ASTM B315
- ASTM B432
- ASTM B96
- ASTM B98
- ASTM B99
- ASTM F467
- SAE J461
- SAE J463
Fabrication and Heat Treatment
Machinability
The machinability rate of UNS C65500 copper alloy is 30.
Welding
The preferred welding techniques of UNS C65500 are soldering, brazing, oxyacetylene welding, gas shielded arc welding, spot welding, coated metal arc welding, seam welding and butt welding.
Forging
UNS C65500 copper alloy is forged at a rating of 40.
Hot Working
UNS C65500 has excellent hot forming capacity.
Cold Working
UNS C65500 copper alloy has excellent cold forming characteristics.
Annealing
UNS C65500 is annealed at temperatures ranging between 482 and 704°C (900 and 1300°F).
Applications
The applications of UNS C65500 copper alloy include:
- Valve guides
- Valve stems
- Fasteners
- Pole line hardware
- Marine fittings